(Georgia Institute of Technology, 2007-01-03)
Wang, Tong
The objective of this work is to electrospin poly(acrylonitrile) (PAN) based nanofibers with controlled diameter and to stabilize and carbonize them for developing meso-porous carbon for application as electrochemical capacitor electrodes. A sacrificial polymer, poly(styrene-co-acrylonitrile) (SAN) has been used to control porosity. Carbon nanotubes (CNT) have been used to increase electrode conductivity and hence power density. The study has been divided into two parts.
In part I, electrospinning behavior of PAN and PAN/CNT has been studied. The diameter of electrospun PAN fibers was monitored as a function of polymer molecular weight, solution concentration, solution flow rate, distance between the spinneret and the target, and the applied voltage. Bead free PAN fibers of 60 nm diameter have been electrospun. Various electrospun fibers have been characterized by wide angle X-ray diffraction and by Raman spectroscopy. Electrospinning process has been observed by high speed photography.
In part II, the electrospun PAN, PAN/SAN, and PAN/SAN/CNT fiber mats were stabilized, carbonized, and processed into electrochemical capacitor electrodes. The performance of the electrochemical capacitors was tested by the constant current charge/discharge and cyclic voltammetry in 6 molar potassium hydroxide aqueous solution. The surface area and pore size distribution of the electrodes were measured using N2 adsorption and desorption. The effect of surface area and pore size distribution on the capacitance performance has been studied. The capacitance performance of various carbonized electrospun fibers mats have been compared to those of the PAN/SAN/CNT film, carbon nanotube bucky paper, and activated carbon pellet. The capacitance of PAN/SAN/CNT fiber mat over 200 F/g (at a current density of 1 A/g) and the power density approaching 1 kW/kg have been observed. Addition of 1 wt% carbon nanotubes in PAN/SAN, improves the power density by a factor of four. For comparison, the capacitance of single wall carbon nanotube bucky paper at a current density of 1 A/g is about 50 F/g.
(Georgia Institute of Technology, 2004-04-12)
Wang, Tong
Carbon nanotubes, and particularly single wall carbon nanotubes (SWNTs) have attracted much attention for their unique structure, as well as for their excellent mechanical, electrical and thermal properties. Most properties of carbon nanotubs are closely related with its anisotropic structure and geometry factor. Characterization of carbon nanotube length is critical for understanding their behavior in solutions as well as in polymer composites. Microscopy, particularly atomic force microscopy, has been used for their length measurement. Microscopy, though straightforward, is quite laborious, particularly for statistically meaningful sampling.
Light scattering can be used to measure particle dimensions. In this study, light scattering has been used to study polyvinyl pyrrolidone (PVP) wrapped SWNTs surfactant assisted aqueous dispersion and SWNT dispersion in oleum. To determine the length of SWNTs, Stokes - Mueller formalism was used, which is a universal model for particles with any size and shape. The Mueller matrix for an ensemble of long, thin cylinders proposed by McClain et al. was used in this study. This Mueller matrix includes the information of size (length and radius) and optical constants (refractive index and extinction coefficient) of cylinders. In this matrix, extinction coefficient, radius and length of SWNTs are unknown. By normalizing scattering intensity I(theta) (theta from 30 to 155 degree) to that at 30degree , the effects of radius and extinction coefficient were cancelled out. Thus, the effect of SWNT length on scattering intensity could be studied independently. A series of curves of normalized scattering intensity of SWNTs (I(theta) /I(30degree)) with varied length as a function of wave vector were predicted. A curve of normalized scattering intensity of SWNT as a function of wave vector was also obtained experimentally. By comparing experimental and predicted curves, average SWNT length in the dispersion has been determined.
Scattering intensity at a given angle initially increases with concentration, and then reaches a critical concentration(C*), above which the scattering intensity decreases. This phenomenon has been attributed to the competition between scattering and absorption of light by the presence of SWNT. By using Beer-Lambert law, this phenomenon has been used to determine the molar absorption coefficient of SWNTs.