Title:
Controlling the crystallization and magnetic properties of melt-spun Pr₂Fe₁₄B/α Fe nanocomposites by Joule heating
Controlling the crystallization and magnetic properties of melt-spun Pr₂Fe₁₄B/α Fe nanocomposites by Joule heating
Authors
Jin, Z. Q.
Cui, B. Z.
Liu, J. Ping
Ding, Yong
Wang, Z. L. (Zhong Lin)
Thadhani, Naresh N.
Cui, B. Z.
Liu, J. Ping
Ding, Yong
Wang, Z. L. (Zhong Lin)
Thadhani, Naresh N.
Authors
Person
Advisors
Advisors
Associated Organizations
Organizational Unit
Organizational Unit
Series
Collections
Supplementary to
Permanent Link
Abstract
Pr₂Fe₁₄B/α Fe based nanocomposites have been prepared through crystallization of melt-spun amorphous Pr₇Tb₁Fe₈₅Nb ₀.₅ Zr ₀.₅ B₆ ribbons by means of ac Joule heating while simultaneously monitoring room-temperature electrical resistance R. The R value shows a strong variation with respect to applied current I, and is closely related to the amorphous-to-nanocrystalline phase transformation. The curve of R versus I allows one to control the crystallization behavior during Joule heating and to identify the heat-treatment conditions for optimum magnetic properties. A coercivity of 550 kA/m and a maximum energy product of 128 kJ/m³ have been obtained upon heating the amorphous ribbons at a current of 2.0 A. These properties are around 30% higher than the values of samples prepared by conventionally (furnace) annealed amorphous ribbons.