Title:
Investigation of Hall effect thruster channel wall erosion mechanisms

dc.contributor.advisor Walker, Mitchell L. R.
dc.contributor.advisor Rimoli, Julian J.
dc.contributor.author Schinder, Aaron M.
dc.contributor.committeeMember Yim, John
dc.contributor.committeeMember Ready, Jud
dc.contributor.committeeMember Simon, Sven
dc.contributor.department Aerospace Engineering
dc.date.accessioned 2017-01-11T14:01:31Z
dc.date.available 2017-01-11T14:01:31Z
dc.date.created 2016-12
dc.date.issued 2016-08-15
dc.date.submitted December 2016
dc.date.updated 2017-01-11T14:01:31Z
dc.description.abstract The primary life-limiting mechanism for Hall effect thrusters (HETs) is the plasma erosion of the discharge channel wall. Over the course of tens of thousands of hours, energetic ions sputter material from the annular discharge channel wall of the HET, wearing away the material in the 1-2 cm near the exit plane of the thruster. If the channel wall is completely worn away in these areas, the magnetic circuit is exposed, and continued operation of the thruster will lead to the ejection of ferrous material into the spacecraft environment and eventual failure of the magnetic circuit. Qualifying HETs for a minimum 1.5 times desired mission life is an expensive process requiring tens of thousands of hours of chamber time. Computational modeling of thruster lifetime can make predictions about the average erosion depth, but present models cannot explain certain features that appear during testing. One such feature is the anomalous erosion ridge phenomenon in HETs. In order to improve HET life modeling, a better understanding of the formation of features during plasma erosion is needed. In this work, an investigation into the details of the plasma erosion of materials is conducted. The way in which the material microstructure and the mechanical stress in materials modify the process of plasma erosion is studied with experiments and computational modeling. A 3D raytracing model of the development of surfaces in a complex heterogeneous material is created. The model reproduces the development of surface features observed in SEM microscopy of the eroded AFRL/UM P5 channel wall. SEM imaging of borosil reveals a complex heterogeneous microstructure composed of boron nitride grains in a silica matrix. The role of the microstructure in the development of observed erosion features is explored. The strain relief hypothesis, which proposes that the presence of mechanical stress in materials will lead to the existence of unstable surface modes under erosion, is investigated. The SRH predicts that surface features with wavelengths dependent on applied mechanical stress will grow during erosion. An experiment to test the dependence of the plasma erosion process on the presence of mechanical stress in materials is designed and conducted. Two materials, amorphous fused silica and M26 borosil, are placed under varying amounts of mechanical stress up to 25 MPa and exposed to argon plasma for 12 hours. Microscopy and detailed surface statistics are collected before and after each exposure. During each exposure, a pair of samples: one under a compressive mechanical load, and the other unloaded, are exposed. The results of these experiments reveal that different mechanisms for each material lead to the development of complex surface patterns. For fused silica, a complex cell pattern is generated from initial roughness present in the surface. The development of this cell pattern can be explained as resulting from the angle-dependence of the sputtering yield of silica. For M26 borosil, it is found that the difference in the sputtering yield between the boron nitride and silica components of the material is the dominant mechanism leading to the development of surface features. For both M26 and fused silica samples, for applied loads of up to 25 MPa, no dependence of the development of the surface features on the mechanical stress has been detected. This work has found that the ion impact angles, the initial surface structure in the case of fused silica, and the heterogeneous nature of borosil composites all play a role in the generation of microstructural surface features during plasma erosion. However, no evidence has been found for the sensitivity of the plasma erosion of M26 and fused silica to mechanical stresses of up to 25 MPa.
dc.description.degree Ph.D.
dc.format.mimetype application/pdf
dc.identifier.uri http://hdl.handle.net/1853/56240
dc.language.iso en_US
dc.publisher Georgia Institute of Technology
dc.subject Electric propulsion
dc.subject Hall effect thrusters
dc.subject HETs
dc.subject Erosion
dc.subject Sputtering
dc.subject Microscopy
dc.subject Channel wall
dc.subject Plasma erosion
dc.title Investigation of Hall effect thruster channel wall erosion mechanisms
dc.type Text
dc.type.genre Dissertation
dspace.entity.type Publication
local.contributor.advisor Walker, Mitchell L. R.
local.contributor.advisor Rimoli, Julian J.
local.contributor.corporatename College of Engineering
local.contributor.corporatename Daniel Guggenheim School of Aerospace Engineering
local.relation.ispartofseries Doctor of Philosophy with a Major in Aerospace Engineering
relation.isAdvisorOfPublication 060e1082-d47d-49ca-b7e3-198c294faa2b
relation.isAdvisorOfPublication 27a85786-1cd4-4655-97d0-ba2c66eccfbc
relation.isOrgUnitOfPublication 7c022d60-21d5-497c-b552-95e489a06569
relation.isOrgUnitOfPublication a348b767-ea7e-4789-af1f-1f1d5925fb65
relation.isSeriesOfPublication f6a932db-1cde-43b5-bcab-bf573da55ed6
thesis.degree.level Doctoral
Files
Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
SCHINDER-DISSERTATION-2016.pdf
Size:
4.96 MB
Format:
Adobe Portable Document Format
Description:
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
LICENSE.txt
Size:
3.87 KB
Format:
Plain Text
Description: