Synthesis and Processing of Nanocrystalline Zirconium Carbide Formed by Carbothermal Reduction
Synthesis and Processing of Nanocrystalline Zirconium Carbide Formed by Carbothermal Reduction
Author(s)
Jain, Anubhav
Advisor(s)
Sacks, Michael D.
Editor(s)
Collections
Supplementary to
Permanent Link
Abstract
Zirconium carbide (ZrC) powders were produced by carbothermal reduction reactions using fine-scale carbon/metal oxide mixtures as the starting materials. The reactant mixtures were prepared by pyrolytic decomposition of solution-derived precursors. The latter precursors were synthesized via hydrolysis/condensation of metal-organic compounds.
The first step in the solution process involved refluxing zirconium alkoxide with 2,4 pentanedione ("acacH") in order to partially or fully convert the zirconium alkoxy groups to a chelated zirconium diketonate structure ("zirconium acac"). This was followed by the addition of water (under acidic conditions) in order to promote hydrolysis/condensation reactions. Precursors with variable carbon/metal ratios were produced by varying the concentrations of the solution reactants (i.e., the zirconium alkoxide, "acacH," water, and acid concentrations.) It was necessary to add a secondary soluble carbon source (i.e., phenolic resin or glycerol) during solution processing in order to obtain a C/Zr molar ratio close to 3 (as required for stoichiometry) in the pyrolyzed powders.
The phase development during carbothermal reduction was investigated for oxide-rich carbon-deficient and slightly carbon-rich compositions. The reaction was substantially completed after heat treatments in the range of ~1400-1500oC. The crystallite sizes were in the range of ~100-130 nm. However, some oxygen dissolved in the lattice and some free carbon was present. Heat treatment at temperatures >1600oC was required to complete the reaction.
The dry-pressed powder compacts, with varying C/Zr molar ratios, were pressureless sintered to relative densities in the range of ~98-100% at 1950oC.